High Adhesion Metallized PET film series（VMPET-GF）
View details >
The High Barrier BOPP Metallized Film VMBOPP-GZ has excellent oxygen and moisture barrier properties as well as excellent adhesion of the aluminum layer. It can replace VMPET or aluminum foil and is used as the middle layer in a three-layer structure, making the composite material homogenous
1:Excellent adhesion of aluminum layer, greatly increasing the composite strength with other materials.
2:Excellent oxygen and moisture barrier properties, extending the shelf life;
3:Replacement of VMPET or aluminum foil, it is used in the middle layer of the three-layer structure to homogenize the composite material.
4:The material complies with FDA, EU, REACH, RoHS and GB4806.7 and other regulatory requirements, and is environmentally friendly, safety and reliability.
1:Excellent adhesion of aluminum layer, greatly increasing the composite strength with other materials.
2:Excellent oxygen and moisture barrier properties, extending the shelf life;
3:Replacement of VMPET or aluminum foil, it is used in the middle layer of the three-layer structure to homogenize the composite material.
4:The material complies with FDA, EU, REACH, RoHS and GB4806.7 and other regulatory requirements, and is environmentally friendly, safety and reliability.
Product Structure
Attention:
In order to maintain the best performance of the material, the material should be stored in
an environment with the temperature below 30°C and a humidity of about 50%RH.
1：In place of aluminum foil and VMPET, better processing performance and enviromental recycling;
2：Application for the pacakge of dried fruits, tea, coffee, chocolate, dehydrated food,dried flavors and fragrances, medicines, etc.
3:Light blocking: Avoid the impact of light on the product, especially on items that are sensitive to light
| 参 数 指 标（型号VMBOPP-GZ） | ||
|---|---|---|
| 测试项目 Test Item | 典型值 Typical value | |
| 厚度 Thickness（μm） | 18 | |
| 光密度 Optical density（OD） | 2.3 | |
| 铝层厚度 Aluminum layer thickness （Ω/□） | 1.2 | |
| 铝层附着力（N/15mm）Aluminum layer adhesion（N/15mm） EAA | 3.5 | |
| 氧气透过率 OTR（cc/m³.24h） | 0.12 | |
| 水蒸气透过率 WVTR（g/m³.24h） | 0.28 | |
| 湿润张力 Wet tension （mN/m） | 镀铝面 Metallized surfece | 42 |
| 非镀铝面 Non-metallized surface | 36 | |
| 拉伸强度（%）Tensile strength%（MPa） | 纵向 MD | 97 |
| 横向 TD | 250 | |
| 断裂伸长率（%）Elongation at break（%） | 纵向 MD | 165 |
| 横向 TD | 33 | |
| 热收缩率（%）Heat shrinkage rate（%）120℃/2min | 纵向 MD | 1.83 |
| 横向 TD | 0.87 | |
Important Notes:
The above data, obtained from our internal testing, is provided for reference only to assist customers in sample evaluation or product use.
The final performance of the product depends on specific production processes, and improper use may cause irreversible damage.
As equipment, processing condtions, and end-use requirements vary across manufacturers, our company shall only be responsible for the
performance of the film itself.