PET-AlOx-D01 is a transparent AlOx-coated BOPET film for packaging that needs both product visibility and barrier performance.

The brochure classifies PET-AlOx-D01 as a no-top-coating, pasteurizable grade. Direct printing is not recommended; printing and lamination surfaces should be confirmed during package trials.

Brochure reference values: 12 μm thickness, OTR ≤ 0.8 cc/m²·day (ASTM D-3985), WVTR ≤ 1.0 g/m²·day (ASTM F-1249), light transmittance ≥ 89%, and pasteurization below 100°C for 30 minutes.

• Transparent barrier film for packages that need product visibility.
• OTR ≤ 0.8 cc/m²·day and WVTR ≤ 1.0 g/m²·day, using the test methods listed in the brochure.
• Light transmittance ≥ 89%.
• 12 μm standard thickness; tensile strength ≥ 170 MPa in MD and TD; elongation at break ≥ 80% in MD and TD.
• Pasteurizable below 100°C for 30 minutes.
• No top coating; direct printing is not recommended for this grade.
• Designed for microwave-heating applications and metal detection, subject to validation of the complete package structure.

• Barrier packaging for meat, cooked food, biscuits, candy, dried fruit, tea, coffee, chocolate, dehydrated food, seafood and flavorings.
• Packaging for pharmaceuticals, cosmetics, daily chemicals and electronic products.
• A transparent barrier option when customers are evaluating alternatives to K-coated films, BOPA, EVOH, co-extruded films, SiOx, aluminum foil or conventional metallized film.
• Final barrier, lamination and pasteurization performance should be validated in the customer's packaging structure.

FAQ

What is PET-AlOx-D01 mainly used for?

The existing page lists transparent barrier packaging for food, electronics, daily chemicals and pharmaceuticals, including pasteurization applications.

What are the key characteristics of this film?

The page describes transparency, oxygen and moisture barrier, aluminum-oxide adhesion, printing and lamination performance, microwave heating and metal detection.

What should buyers confirm before ordering?

Buyers should confirm thickness, barrier requirements, aluminum-oxide adhesion, pasteurization conditions and the intended packaging structure.