Singled Side Matte PET Metallized Film
View details >
Material PET Thickness 12um/Customized Length customized Width customized Certificate FDA、EU、REACH、RoHS Packing Wooden pallets MOQ 1 Metric Ton
Semipermeable polyester aluminum-coated film, also known as semipermeable electronic film, due to its conductivity and anti-static properties, as well as its transparency, when combined into bags, the contents can be seen clearly. The aluminum layer is very thin; it has a brightness, good flatness and friction coefficient.
1. It possesses the unique conductive property of the aluminized film, as well as transparency. When laminated into a bag, the contents can be clearly seen.
2. Anti-ultraviolet, anti-static.
3. It has the function of resisting static electricity and blocking electromagnetic wave interference.
The product is widely used in the outer packaging bags of electronic products.
| 参考标准 | 常用产品型 | ||||||
| DZ-15 | DZ-16 | DZ-18 | DZ-22 | ||||
| 物性项目 | 测试方法 | 单位 | 标准值 | 标准值 | 标准值 | 标准值 | |
| 厚度 | GB/T 6672-2001 | 12 | 12 | 12 | 12 | 12 | |
| 拉伸强度 | MD | GB/T 1040.3 | MPa | ≥170 | ≥170 | ≥170 | ≥170 |
| TD | ≥170 | ≥170 | ≥170 | ≥170 | |||
| 断裂伸长率 | MD | GB/T 1040.3 | % | ≤200 | ≤200 | ≤200 | Standard Item No. DZ-15 DZ-16 DZ-18 DZ-22 Item Testing methods Unit Typical Value Typical Value Typical Value Typical Value Thickness GB/T 6672-2001 12 12 12 12 12 Tensile Strength MD ≥170 ≥170 MPa ≥170 ≥170 ≥170 ≥170 TD ≥170 ≥170 ≥170 ≥170 Elongation at Break MD ≤200 ≤200 % ≤200 ≤200 ≤200 ≤200 TD ≤200 ≤200 ≤200 ≤200 Heat Shrinkage MD ≤3.0 ≤3.0 % ≤3.0 ≤3.0 ≤3.0 ≤3.0 TD ≤3.0 ≤3.0 ≤3.0 ≤3.0 Surface Tension Al side ≥48 ≥42 mN/m ≥48 ≥170 ≥48 ≥48 Non Al side ≥42 ≥170 ≥42 ≥42 Light Transmittance 林尚SL162 % 35-40% 40-45% 45-50% 65-70% Haze ASTM D-1003 % ≤3.0 ≤3.0 ≤3.0 ≤3.0 Al Uniformity ASTM D-1003 % 5 5 5 5 Al Adhesion QB/T 2358-1998 N/15mm 2.5 2.5 2.5 2.5 Technical Index Customers can customize production from 0 to 80% light transmittance according to demand. |
| TD | ≤200 | ≤200 | ≤200 | ≤200 | |||
| 热收缩率 | MD | 150ºC*30min | % | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 |
| TD | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 | |||
| 湿润张力 | 镀层面 | 150ºC*30min | mN/m | ≥48 | ≥170 | ≥48 | ≥48 |
| 非镀层面 | ≥42 | ≥170 | ≥42 | ≥42 | |||
| 透光率 | 林尚SL162 | % | 35-40% | 40-45% | 45-50% | 65-70% | |
| 基膜雾度 | ASTM D-1003 | % | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 | |
| 镀层均匀度 | ASTM D-1003 | % | 5 | 5 | 5 | 5 | |
| 镀层附着力 | QB/T 2358-1998 | N/15mm | 2.5 | 2.5 | 2.5 | 2.5 | |
Important Tips：
1.The data and ,information above are obtained from our company's tests, for customers' reference of sample or the product usage;
2.The final performance of the product is related to the composite process,and improper use will cause destructive damage to the product;
3.For other special requirements,it is better to contact with our technical department for more details,so that the products are more suitable for customers.